Wang, Q.*; Ma, N.*; Huang, W.*; Shi, J.*; Luo, X.-T.*; 冨高 宙*; 諸岡 聡; 渡邊 誠*
Materials Research Letters (Internet), 11(9), p.742 - 748, 2023/09
Cold spray (CS) has emerged as a representative of solid-state additive manufacturing (AM) via supersonic impact. It enables a high deposition rate of solid-state microparticles. Delamination, however, tends to occur when depositing too thick; this remains to be conquered. Here, a CS-like process, warm spray (WS), was presented. Interestingly, it was found that the appropriate increase in particle temperature can effectively reduce the residual stress amplitude, relieving the concentrated tensile stress and safeguarding the additively manufactured components from interfacial delamination even when depositing too thick. The key role of temperature on delamination was identified in solid-state AM via supersonic impact.
馬場 信一; 石原 正博; 皆川 宣明; 鈴木 淳市
Proceedings of International Conference on Advanced Technology in Experimental Mechanics 2003 (ATEM '03) (CD-ROM), 4 Pages, 2003/09
本論文の目的は、円筒型の炭素繊維強化炭素複合材料の製造過程で発生した層間剥離(クラック)の原因である残留応力分布を明らかにすることである。残留応力の測定は日本原子力研究所の第3号原子炉に付設した中性子散乱実験施設の残留応力測定装置(RESA)を用いて行った。残留応力測定の結果、円筒型炭素複合材料の内部には圧縮応力が分布しており、その巨視的な残留歪み/応力はおもに材料内部に分布している気孔の変形として吸収されることがわかった。